الخلاصة:
Nowadays, nanostructures, characterized by their excellent mechanical, electronic, optical and
thermal properties as well as the advantages from their extremely small feature size, are worldwide
investigated. Particular interest is shown for one-dimensional semiconductor nanostructures, such as
nanowires (NWs), due to their potentially innovative applications in nanoelectromechanical
systems. Consequently, several approaches and diffraction techniques (TEM, STM, AFM, etc.)
have been developed to study experimentally and theoretically their mechanical behavior. However,
few data were reported on such properties via nondestructive methods. In this context, we consider
the scanning acoustic microscope technique, SAM, based on the propagation of ultrasonic waves to
predict their elastic properties. To do so, we chose individual coaxial SiC(core)/SiO2(sheathed
layer) nanowires to investigate the effects of sheath diameters (Ds) and core diameters (Dc) on
several acoustic parameters.The calculation methodology consists of several steps: determination of
longitudinal and transverse wave velocities, calculation of refection coefficients, calculation of
acoustic signatures, V (z), and Rayleigh velocity determination. Qualitatively, the usual oscillatory
behavior of acoustic signatures was clearly obtained due to constructive and destructive interference
between different modes. Quantitatively, it was found that changes in SiC/SiO2 NW diameters over
the ranges: 51 nm ≤ Ds ≤ 200 nm and 12 nm ≤ Dc ≤ 100 nm lead to variations of (i) critical angles
of longitudinal mode from 8.3° to 6.2°, transversal mode from 15.6° to 11.5° and Rayleigh mode
from 16.1° to 12.0°, (ii) acoustic impedances of longitudinal modefrom 11.9 Mrayl to 15.5 Mrayl
and transversal mode from 6.6 Mrayl to 8.5 Mrayl, (iii) space periods in periodic V(z) curves varies
from 59.8 μm to 118 μm, and (iv) longitudinal velocity from 5166 m/s to 6947 m/s, transverse
velocity from 2793 m/s to 3756 m/s and Rayleigh velocity from 2597 m/s to 3493 m/s. For
comparison, elastic parameters of both bulk pure SiO2 and SiC are also computed to find that the
acoustic values deduced for bulk pure SiO2 are in good agreement with those obtained for the
highest diameters of SiC/SiO2 nanowires. Furthermore, to enrich this investigation, all the above
variations were quantified via curve fitting to deduce semi-empirical relations that can be used to
predict elastic properties of such nanomaterials by just knowing their diameters and vice versa